NFS-L-8400系列雙組份加成型液體氟矽橡膠具有優異的耐高低溫性、耐油性和電氣絕緣性,可用於製作汽車工業、航空航天、電力電氣、消費電子、穿戴用品等領域的耐油橡膠製品。
項目 |
測試方法 |
NFS-L-8440 |
NFS-L-8460 |
A組份顏色 |
目測 |
淡黃色 |
淡黃色 |
B組份顏色 |
目測 |
淡黃色 |
淡黃色 |
A組份粘度/Pa.s(剪切速率10 s-1) |
Q/371002WXH028-2016 |
700 |
820 |
B組份粘度/Pa.s(剪切速率10 s-1) |
Q/371002WXH028-2016 |
650 |
770 |
120℃×10min一次硫化後 |
|||
密度/g/cm3 |
ASTM D792 |
1.43 |
1.42 |
硬度/Shore A |
ASTM D2240 |
39 |
59 |
拉伸強度/MPa |
ASTM D412 |
11.0 |
7.9 |
斷裂伸長率/% |
ASTM D412 |
425 |
235 |
撕裂強度/kN/m |
ASTM D624-B |
15 |
13 |
回彈性/% |
ASTM D1054 |
40 |
41 |
壓縮永久變形/%(177℃×22h) |
ASTM D395 |
10 |
20 |
200℃×4h二次硫化後 |
|||
硬度/Shore A |
ASTM D2240 |
40 |
62 |
拉伸強度/MPa |
ASTM D412 |
10.8 |
7.2 |
斷裂伸長率/% |
ASTM D412 |
368 |
181 |
撕裂強度/kN/m |
ASTM D624-B |
14 |
13 |
回彈性/% |
ASTM D1054 |
41 |
43 |
壓縮永久變形/%(177℃×22h) |
ASTM D395 |
4 |
6 |
耐油性 |
|||
Dextron III/%(125℃×168h) |
ASTM D471 |
1.1 |
1.2 |
IRM903/%(150℃×168h) |
ASTM D471 |
2.2 |
2.0 |
RME Biodiesel/%(40℃×168h) |
ASTM D471 |
3.1 |
3.2 |
Fuel F Diesel/%(40℃×168h) |
ASTM D471 |
3.3 |
2.4 |
Fuel C/%(60℃×168h) |
ASTM D471 |
22.2 |
20.5 |
FAM B/%(60℃×168h) |
ASTM D471 |
28.8 |
28.0 |
Jet Fuel No.3/%(23℃×168h) |
ASTM D471 |
4.9 |
5.1 |
硫化條件:
NFS-L-8440液體氟矽橡膠的硫化時間取決於硫化溫度及硫化產品的厚度和大小,當硫化產品加熱至120℃時,可在幾秒內迅速硫化,速率可根據部件尺寸進行優化,建議硫化條件為一次硫化120℃×10min,二次硫化200℃×4h,請按實際生產工藝合理調整硫化時間。
包裝:
塑料桶包裝,A/B組份各20kg單獨包裝。
貯存期:
存放於陰涼乾燥的環境,未開封原包裝中貯存期十二個月。
注意事項:
避免與含氮、硫、磷及重金屬等元素的化合物接觸,以免引起產品硫化不熟或不硫化情況。